铝合金焊接工艺规范目录(工作试样)
序号[***********][***********][***********][***********]1
WPS №SFW-A-701SFW-A-702SFW-A-703SFW-A-704SFW-A-705SFW-A-706SFW-A-707SFW-A-708SFW-A-709SFW-A-710SFW-A-711SFW-A-712SFW-A-713SFW-A-714SFW-A-715SFW-A-716SFW-A-717SFW-A-718SFW-A-719SFW-A-720SFW-A-721SFW-A-722SFW-A-723SFW-A-724SFW-A-725SFW-A-726SFW-A-727SFW-A-728SFW-A-729SFW-A-730SFW-A-731
部位名称
枕梁-牵引梁(下面)枕梁-牵引梁(上面)枕梁内部补强
LV座三角补强-边梁枕梁-边梁
LV座三角补强-枕梁LV座三角补强-LV座减震器座上板-枕梁减震器座上板-小横梁减震器座侧板-枕梁减震器座下板-枕梁减震器座补强1减震器座补强2
减震器座下板-边梁减震器座下板-补强减震器座补强-枕梁门立柱-门角1门立柱-门角2
枕梁三角补强(牵引梁侧)枕梁三角补强(枕梁侧)枕梁上盖板自动焊枕梁下盖板自动焊卧铺安装座1卧铺安装座2
侧墙与车顶连接内部侧墙与底架连接内部司机室外皮板2.5司机室外皮板2.5门袋支柱与外板门角部加强件头车车顶安装垫片
厚度组合mm
试板材质组合
接头形式レ型对接レ型对接レ型角接角接レ型角接レ型角接角接レ型角接レ型角接レ型角接レ型角接レ型角接レ型对接レ型角接レ型角接レ型对接レ型对接レ型对接レ型对接对接对接搭接搭接对接角接I型对接I型对接I型对接I型对接卷边
焊接姿势
11+1015+1115+1012+510+412+1212+612+1012+412+1010+1212+1215+1222+522+1215+1235+1035+712+812+106+1015+155+35+23+34+52.5+2.52.5+2.56+2.56+356+2.5A7N01S-T5+A7N01S-T5A7N01S-T5+A7N01S-T5A7N01S-T5+A7N01S-T5A7N01P-T4+A6N01S-T5A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01P-T4A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01S-T5+A7N01P-T4A7N01P-T4+A7N01P-T4A7N01P-T4+A7N01P-T4A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01S-T5+A7N01P-T4A7N01S-T5+A6N01S-T5A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A5083P-O+A6N01S-T5A5083P-O+A6N01S-T5A6N01S-T5+A6N01S-T5A6N01S-T5+A6N01S-T5A5083P-O+A5083P-OA5083P-O+A5083P-OA5083P-O+A6N01S-T5A5083P-O+A7N01P-T4A5083P-O+A6N01S-T5平焊平焊平焊平焊平焊平焊平焊平焊平焊立焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊仰焊平焊立焊横焊平焊平焊平焊
焊接工艺规范
南车青岛四方股份公司WPQR编号
/
WPS编号
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-719
2009.5.27
版本
ver 1
接头种类及焊缝种类:对接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A7N01P-T4+A7N01S-T5材料厚度(mm):12+8
部位名称:枕梁三角补强(牵引梁侧)
宏观金相
S2S1F2F1
焊接工艺规范参数
焊道F1F2S1S2
焊接方法脉冲MIG脉冲MIG脉冲MIG脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接直流反接直流反接直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.61.61.61.6
[1**********]5
26252527
////
35403030
10,2518,62511,50012,150
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:背部清根预热温度:/
层间温度:50℃~70℃
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/振幅:/焊枪角度:5°
焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-723
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):5+3部位名称:卧铺安装座1
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219021/405,985
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-724
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):5+2部位名称:卧铺安装座2
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.218020/405,400
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-725
2009.5.27
版本
ver 1
接头种类及焊缝种类:对接焊接位置:仰焊( PE )焊缝制备细节(草图)
接头简图
母材规程:A6N01S-T5材料厚度(mm):3
部位名称:侧墙与车顶连接内部
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219022/406,270
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-726
2009.5.27
版本
ver 1
接头种类及焊缝种类:角接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A6N01S-T5材料厚度(mm):3
部位名称:侧墙与底架连接内部
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.221024/605,040
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-727
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:立焊( PF )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O材料厚度(mm):2.5+2.5部位名称:司机室外皮板2.5
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.212017/552,225
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/
振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-728
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:横焊( PC )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O材料厚度(mm):2.5+2.5部位名称:司机室外皮板2.5
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.211519/502,622
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/
振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-729
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PA )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):6+2.5部位名称:门袋支柱与外板
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.216520/355,657
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-730
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PA )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A7N01P-T4材料厚度(mm):6+35部位名称:门角部加强件
宏观金相
F1S1
焊接工艺规范参数
焊道F1S1
焊接方法脉冲MIG脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.21.2
230230
2323
//
6070
5,2904,534
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/
层间温度:50℃~70℃
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
标记处数修改文件号签字日期标记处数修改文件号签字日期
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-731
2009.5.27
版本
ver 1
接头种类及焊缝种类:卷边焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):6+2.5部位名称:头车车顶安装垫片
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219023/505,244
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
标记处数修改文件号签字日期标记处数修改文件号签字日期
铝合金焊接工艺规范目录(工作试样)
序号[***********][***********][***********][***********]1
WPS №SFW-A-701SFW-A-702SFW-A-703SFW-A-704SFW-A-705SFW-A-706SFW-A-707SFW-A-708SFW-A-709SFW-A-710SFW-A-711SFW-A-712SFW-A-713SFW-A-714SFW-A-715SFW-A-716SFW-A-717SFW-A-718SFW-A-719SFW-A-720SFW-A-721SFW-A-722SFW-A-723SFW-A-724SFW-A-725SFW-A-726SFW-A-727SFW-A-728SFW-A-729SFW-A-730SFW-A-731
部位名称
枕梁-牵引梁(下面)枕梁-牵引梁(上面)枕梁内部补强
LV座三角补强-边梁枕梁-边梁
LV座三角补强-枕梁LV座三角补强-LV座减震器座上板-枕梁减震器座上板-小横梁减震器座侧板-枕梁减震器座下板-枕梁减震器座补强1减震器座补强2
减震器座下板-边梁减震器座下板-补强减震器座补强-枕梁门立柱-门角1门立柱-门角2
枕梁三角补强(牵引梁侧)枕梁三角补强(枕梁侧)枕梁上盖板自动焊枕梁下盖板自动焊卧铺安装座1卧铺安装座2
侧墙与车顶连接内部侧墙与底架连接内部司机室外皮板2.5司机室外皮板2.5门袋支柱与外板门角部加强件头车车顶安装垫片
厚度组合mm
试板材质组合
接头形式レ型对接レ型对接レ型角接角接レ型角接レ型角接角接レ型角接レ型角接レ型角接レ型角接レ型角接レ型对接レ型角接レ型角接レ型对接レ型对接レ型对接レ型对接对接对接搭接搭接对接角接I型对接I型对接I型对接I型对接卷边
焊接姿势
11+1015+1115+1012+510+412+1212+612+1012+412+1010+1212+1215+1222+522+1215+1235+1035+712+812+106+1015+155+35+23+34+52.5+2.52.5+2.56+2.56+356+2.5A7N01S-T5+A7N01S-T5A7N01S-T5+A7N01S-T5A7N01S-T5+A7N01S-T5A7N01P-T4+A6N01S-T5A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01P-T4A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01S-T5+A7N01P-T4A7N01P-T4+A7N01P-T4A7N01P-T4+A7N01P-T4A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01S-T5+A7N01P-T4A7N01S-T5+A6N01S-T5A7N01S-T5+A6N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A7N01P-T4+A7N01S-T5A5083P-O+A6N01S-T5A5083P-O+A6N01S-T5A6N01S-T5+A6N01S-T5A6N01S-T5+A6N01S-T5A5083P-O+A5083P-OA5083P-O+A5083P-OA5083P-O+A6N01S-T5A5083P-O+A7N01P-T4A5083P-O+A6N01S-T5平焊平焊平焊平焊平焊平焊平焊平焊平焊立焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊平焊仰焊平焊立焊横焊平焊平焊平焊
焊接工艺规范
南车青岛四方股份公司WPQR编号
/
WPS编号
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-719
2009.5.27
版本
ver 1
接头种类及焊缝种类:对接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A7N01P-T4+A7N01S-T5材料厚度(mm):12+8
部位名称:枕梁三角补强(牵引梁侧)
宏观金相
S2S1F2F1
焊接工艺规范参数
焊道F1F2S1S2
焊接方法脉冲MIG脉冲MIG脉冲MIG脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接直流反接直流反接直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.61.61.61.6
[1**********]5
26252527
////
35403030
10,2518,62511,50012,150
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:背部清根预热温度:/
层间温度:50℃~70℃
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/振幅:/焊枪角度:5°
焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-723
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):5+3部位名称:卧铺安装座1
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219021/405,985
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-724
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):5+2部位名称:卧铺安装座2
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.218020/405,400
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-725
2009.5.27
版本
ver 1
接头种类及焊缝种类:对接焊接位置:仰焊( PE )焊缝制备细节(草图)
接头简图
母材规程:A6N01S-T5材料厚度(mm):3
部位名称:侧墙与车顶连接内部
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219022/406,270
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-726
2009.5.27
版本
ver 1
接头种类及焊缝种类:角接焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A6N01S-T5材料厚度(mm):3
部位名称:侧墙与底架连接内部
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.221024/605,040
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-727
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:立焊( PF )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O材料厚度(mm):2.5+2.5部位名称:司机室外皮板2.5
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.212017/552,225
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/脉冲频率:/
振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-728
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:横焊( PC )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O材料厚度(mm):2.5+2.5部位名称:司机室外皮板2.5
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.211519/502,622
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/
振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-729
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PA )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):6+2.5部位名称:门袋支柱与外板
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.216520/355,657
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-730
2009.5.27
版本
ver 1
接头种类及焊缝种类:搭接焊接位置:平焊( PA )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A7N01P-T4材料厚度(mm):6+35部位名称:门角部加强件
宏观金相
F1S1
焊接工艺规范参数
焊道F1S1
焊接方法脉冲MIG脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.21.2
230230
2323
//
6070
5,2904,534
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/
层间温度:50℃~70℃
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
标记处数修改文件号签字日期标记处数修改文件号签字日期
南车青岛四方股份公司WPQR编号
/
Welding Procedure Specification
执行标准
ISO 15614-2:2004
日期
SFW-A-731
2009.5.27
版本
ver 1
接头种类及焊缝种类:卷边焊接位置:平焊( PB )焊缝制备细节(草图)
接头简图
母材规程:A5083P-O+A6N01S-T5材料厚度(mm):6+2.5部位名称:头车车顶安装垫片
宏观金相
F1
焊接工艺规范参数
焊道F1
焊接方法脉冲MIG
焊丝直径
mm
电流I
A
电压U
V
电流种类/极性直流反接
送丝速度
m/min
焊接速度V
cm/min
热输入H
J/cm
1.219023/505,244
保护气体/焊剂
电弧保护根部保护
Ar 99.999%
/
气体流量(L/min)
电弧保护根部保护
24/
注:a) 焊接电流、焊接电压、焊接速度允许上下浮动10%; b) H=60UI/V。
焊接材料标识及制造:ER5356特殊衬垫或烘干:/钨极种类及尺寸:/清根/衬垫的细节:/预热温度:/层间温度:/
制备及清理方法:有机溶剂+机械清理
其他说明:
基值电流:/
脉冲频率:/振幅:/
焊枪角度:5°焊后热处理:
时间、温度、方法:/加热和冷却速度:/加热和冷却速度:/
标记处数修改文件号签字日期标记处数修改文件号签字日期